1. Configure Advantage Tactile Systems - Tactile Warning Surfaces:
Stainless Steel Detectable/Tactile Warning Surface Tiles:
Dimensions:
Color:
Performance Standards: Comply with the following:
Slip Resistance of Tile when tested by ASTM C 1028 the combined Wet and Dry Static Co-Efficients of Friction not to be less than 0.80 on top of domes
and field area.
Chemical Stain Resistance of Tile when tested by ASTM D 543 to withstand without discoloration or staining - saturated calcium chloride, red enamel
spray paint, red lipstick, red wax crayon, black liquid ink, chewing gum, mustard, ketchup, urine, coffee, diesel fuel, asphalt, tobacco juice, hydraulic oil
and motor oil.
Abrasive Wear of Tile when tested by BYK - Gardener Tester ASTM D 2486 with reciprocating linear motion of 37 plus or minus cycles per minute
over a 10 inches of travel The abrasive medium, a 40 grit Norton Metallite sand paper, to be fixed and leveled to a holder. The combined mass
of sled, weight and wood block is to be 3.2 lb. Average wear depth shall not exceed 0.010 inch after 1,000 abrasion cycles when measured on the top
surface of the dome representing the average of three measurement locations per sample.
Abrasive Wear of Tile when tested by Taber Tester ASTM C 501 and Federal Specifications SS-T-308b with H22 coarse Calibrade Wheels with each testing
coupon weighed to the nearest 0.01 gram Average wear index shall be a minimum of 480 after 1,000 abrasion cycles with ASTM C 501 parameters
and 210 with SS-T-308b parameters when measured on the top surface of the dome representing the average of four sample measurements.
Gardner Impact to Geometry "GE" of the standard when tested by ASTM D 5420 to have a mean failure energy expressed as a function of specimen
thickness of not less than 550 in. lbf/in A failure is noted when a crack is visible in coating or a 3 mm depression on domes for coated tile.
Accelerated Weathering of Tile when tested by ASTM G 155 for 3,000 hours shall exhibit the following result - E <2.6, as well as no deterioration,
fading or chalking of surface of federal yellow color tile (federal No. 33538).
Accelerated Aging and Freeze Thaw Test of Tile and Adhesive System when tested to ASTM D 1037 shall show no evidence of cracking, delamination,
warpage, checking, blistering, color change, loosening of tiles or other detrimental defects.
Salt and Spray Performance of Tile when tested to ASTM B 117 not to show any deterioration or other defects after 1,000 hours of exposure.
Tensile Strength of Concrete Repair and Overlay Materials by Direct Pull-off Method ASTM C 153 tensile bond strength shall not be less than 160 psi.
Determining the Adhesion of Lamination Films to Prints Utilizing Mechanical Stress by Four Different Test Methods - Score/Tape, Cross Hatch,
X-Cut, and Crease Folding by ASTM F 2296 not to show any failure of coating delaminating from metal panel.
Crazing resistance by thermal shock with breaches in coating by ASTM C 554 no failure up to 450 degrees Fahrenheit.
AASHTO HB-17 single wheel HS20-44 loading "Standard Specifications for Highways and Bridges". The Cast In Place Tile shall be mounted on
a concrete platform then subjected to the specified maximum load of 10,400 lbs., corresponding to an 8,000 lb individual wheel load and
a 30 percent impact factor. The tile shall exhibit no visible damage at the maximum load of 10,400 lbs".