1. Maxxon Corporation - CEMENTITIOUS UNDERLAYMENT:

Cementitious Underlayment

Maxxon Level-Right

Material: Hydraulic cement

Dry Density: Approximately 125 pcf (2003 kg/cu.m)

Compressive Strength, per modified ASTM C 109, at 28 days: 5500 psi (38 MPa).

Flexural Strength: Tensile Strength, per ASTM C 348, at 28 days: 1260 psi (8.7 MPa)

Tensile Strength, per ASTM C 190, at 28 days: 720 psi (5 MPa)

Maxxon Level-Right PLUS

Material: Polymer modified hydraulic cement

Dry Density: Approximately 120-125 pcf (1922 - 2003 kg/m3)

Compressive Strength, per modified ASTM C 109, at 28 days: 5500 - 7000 psi (38-48 MPa)

Flexural Strength: Tensile Strength, per ASTM C 348, at 28 days: 1250 psi (8.6 MPa)

Tensile Strength, per ASTM C 190, at 28 days: 810 psi (6 MPa)

Maxxon Level-Right FS-10

Material: Polymer modified hydraulic cement.

Dry Density: Approximately 120-125 pcf (1922 - 2003 kg/m3)

Compressive Strength, per modified ASTM C 109, at 28 days: 5500 - 7200 psi (38-50 MPa)

Tensile Strength, per ASTM C 190, at 28 days: 1200 psi (8.3 MPa)

Cementitious Topping

Maxxon Level-Right WearTop

Material: Polymer modified hydraulic cement

Dry Density: Approximately 120 pcf (1920 kg/cu.m)

Compressive Strength, per modified ASTM C 109, at 28 days: 6200 psi (43 MPa)

Flexural Strength: Tensile Strength, per ASTM C 348, at 28 days: 1440 psi (10 MPa)

Tensile Strength, per ASTM C 190, at 28 days: 810 psi (6 MPa)